6mm Ultra-Thin Silicon Carbide Ceramic Tile with NIJ Level III Protection and High Density Microstructure
Produktdetails:
| Herkunftsort: | Hunan, China |
| Markenname: | High Broad |
| Zertifizierung: | ISO 9001:2015, NIJ 0101.06 |
| Modellnummer: | sic Fliesen |
| Dokumentieren: | SIC Ballistic Armor Tiles-P...ad.pdf |
Zahlung und Versand AGB:
| Min Bestellmenge: | 1000 Stück |
|---|---|
| Preis: | USD 0.1-1 / Piece |
| Verpackung Informationen: | Einzelner EPE-Schaumstoffeinsatz + vakuumversiegelter antistatischer Beutel + Export-Sperrholzkiste |
| Lieferzeit: | 5–7 Werktage für den Lagerbestand, 15–20 Tage für die Produktion |
| Zahlungsbedingungen: | T/T, L/C, Western Union |
| Versorgungsmaterial-Fähigkeit: | 2500000 Stück pro Monat |
|
Detailinformationen |
|||
| Dichte: | 3,12-3,18 g/cm³ | Härte (GPa): | 25-28 |
|---|---|---|---|
| Biegefestigkeit: | 400-480 MPa | Fliesengröße: | 100x100 mm |
| Flächendichte: | ≤28 kg/m² | Bruchzähigkeit: | 3,8–4,8 MPa·m½ |
| Hervorheben: | Ultra Thin SiC Tile,Lightweight Strike Face Plate,NIJ III Thin Armor Ceramic |
||
Produkt-Beschreibung
- 6mm Ultra-Thin Profile
- High Density Microstructure
The HB achieves NIJ Level III protection with just 6mm ceramic thickness—a 25% reduction from standard 8mm tiles. This is made possible through our advanced high-density pressureless sintering process that produces SiC with 3.15+ g/cm³ density and 2600+ HV hardness, approaching hot-pressed density values without the associated cost premium. The result: armor systems that are significantly lighter and thinner without compromising protection.
| Ceramic Type | Required Thickness | Areal Density @ NIJ III | Weight Index |
|---|---|---|---|
| HB SiC (6mm high-density) | 6.0 mm | ≤ 28 kg/m² | ★★★ Best |
| Standard SiC (8mm) | 8.0 mm | ~36 kg/m² | ★★ Good |
| Alumina Al2O3 (10mm) | 10.0 mm | ~42 kg/m² | ★ Heavy |
| Boron Carbide B4C (6mm) | 6.0 mm | ~22 kg/m² | ★★★★ Lightest (High Cost) |
WNRLN 6mm SiC achieves the optimal balance: B4C-level thinness at 50-60% lower cost.
Our controlled-atmosphere pressureless sintering process achieves 98.5%+ theoretical density with minimal porosity (<0.5%), enabling the thinner profile without strength compromise.
The 6mm ultra-thin profile and 28 kg/m² areal density make this tile ideal for helicopter crew seats, vehicle spall liners, and portable shield applications where weight budget is critical.
Double-side ground to ≤20μm flatness and ≤0.8μm Ra surface finish, ensuring uniform adhesive bond line thickness across the entire tile surface.
Despite the thin profile, enhanced fracture toughness (3.8-4.8 MPa*m½) ensures reliable multi-hit performance. Tested with 3-round triangular shot pattern at 50mm spacing.
Technical datasheets and ballistic test reports available